Area of Use
Ideal for surface cleaning of very thin (2 mm thick) steel plate and profiles, cleaning of stainless steel castings and metal plate, production of bright steel parts, cleaning of nutsmand bolts, cleaning of non-ferrous metals
- Oxide and Scale removal from thin steel plate and profiles
- Surface preparation of bright steel parts
- Cleaning of aluminum castings
- Cleaning of stainless steel plate
- Cleaning of stainless steel castings
- Cleaning of nuts and bolts prior to coating.
|
||||||||||
| 30 | 0,60 | 0,023 | All pass | |||||||
| 35 | 0,50 | 0,0197 | 10% max | |||||||
| 40 | 0,42 | 0,017 | - | |||||||
| 45 | 0,35 | 0,014 | - | |||||||
| 50 | 0,30 | 0,012 | 80% min | |||||||
| 80 | 0,18 | 0,007 | 90% min | |||||||
| 120 | 0,12 | 0,005 | - | |||||||
Chemical Analysis |
|
| Carbon | % 0,10 - % 0,15 |
| Manganese | % 1,20 - % 1,50 |
| Silicon | % 0,10 - % 0,25 |
| Sulphur | max. % 0,035 |
| Phosphorus | max. % 0,035 |
Hardness
TOÇELİK LOW CARBON STEEL SHOT is subject to hardness testing that requires at least 90% of the shot sample falling within the range of 43-44 HRC.
Density
Density must be 7.0 g / cm3 minimum
Microstructure
As a result of the bainitic microstructure, TOSÇELİK LOW CARBON STEEL SHOT has a higher level of hardness and greater service life.
General Look
Steel Shot is required to be in a spherical form as much as possible. Extended or compound particles, tails, hollows, broken pieces, shrinkage, slag and dirt have to be at a minimum level.
Applications
Sectors
Steel shot is mainly used in foundries, steel mills, forging shops, rolling mills, machine shops, structural steel mills that are serving automotive, construction, ship building, aerospace, agriculture and many other industries.
Applications
Sand Removal, Deburring, Descaling, Oxide Removal, Surface Treatment, Stress Relieving, Shot Peening